mordashka
Magnetics Epcos (Siemens Matsushita Components), Germany TDK Ferroxcube
North West Laboratory

Engineering Center SZL and LEPCOS
— General representative of Epcos AG by ferrite in the CIS
— Official distributor and general representative for ferrites of
    TDK Electronics Europe Gmbh in the CIS
— Authorized distributor of Magnetics in Russia, CIS and Baltic countries
— Exclusive distributor of USM in Russia and CIS countries
— Official Distributor Temex Ceramics in Russia and CIS
 
Articles » FAQs (Magnetics) »

FAQs (Magnetics)

Magnetics experts made a review list of frequently asked questions. For a comfortable searching of the required answers one can choose a corresponding section.

  1. General information
  2. Application
  3. Assembly
  4. Powder cores
  5. Ferrites

We hope, that represented answers will be useful for your practice in the field of magnetic materials.

General information

How do you test for AL?

Inductance is measured on a bridge with variable voltage and frequency. The flux density should be less than 10 gauss. Cores have to be properly mounted around the measuring coil, or for toroids, wound with the correct number of turns.

Testing at low gauss level is important. Magnetic material characteristics change considerably at higher drive levels. Since all applications are different, it is necessary for manufacturers to normalize characteristics at a low level to insure a degree of consistency in magnetic properties and that "apples are compared to apples."

Why is corner radius important on a toroid?

A radius is important on a toroid because if the core has sharp edges, the wire insulation could be scraped during rigorous winding operations. Magnetics takes special pains to insure that toroids have some radius. Ferrite toroid dies are made with a built-in radius, and cores are tumbled to remove any sharp edges. Powder cores have a radius on one side of the tool and the other side is deburred. Additionally many cores are painted or coated to provide not only a more blunt corner radius, but also a smoother winding surface. As with ferrites, a coating provides additional edge coverage.

Why do you provide AL for ferrites and powder cores and not for tape cores?

Tape wound cores are generally used in transformer or square loop applications in which AL is not critical. The desirable characteristics are high flux density, low core losses, and in some cases high squareness in the B-H loop. In square B-H loop materials such as those used in tape wound cores, the permeability varies widely as the loop is traversed; a consistent and repeatable inductance measurement is not obtainable. In rounded B-H loop materials, such as ferrites and powder cores, the permeability is more constant along the loop. AL is a measure of permeability at low drive levels, where the permeability is relatively stable in round loop materials.

Can I get tighter dimensional tolerances on cores?

During the sintering operation, ferrite parts shrink to their final dimensions. Different material and processing techniques result in variance in this linear shrinkage which can range from 10 to 20% of the pressed dimensions. The resulting variation in fired dimensions results in final tolerances in the range of 1-4%. Some dimensions cannot be held to a tighter tolerance. But dimensions that can be machined after firing can certainly be held to tighter tolerances. Powder cores generally have the dimensions held to the best available tolerances, though custom dimensions can be quoted on special specification parts.

What is the best core shape?

There is no "best shape" It depends on the application, space constraints, temperature limitations, winding capabilities, assembly, and a number of other factors; this means compromises must be made.

Why are AL tolerances wide for ferrites and narrow for powder cores?

Ferrites are sensitive to chemistry and kiln conditions. Fired cores have wide inductance tolerances, but machining an air gap in the core provides a tighter AL. Process control in ferrite manufacturing results in inductance ranges ±20% to ±30% (without 100% selection), in the case of ungapped cores. Process control in powder core manufacturing results in inductance ranges of ±8% to ±15%.

Can you tighten electrical tolerances on toroidal cores?

While a production batch of toroids may have a wide tolerance, the cores can be graded into narrower inductance bands. Powder cores are all ±15% or better. MPP and High Flux are graded into 2% bands. Due to the equipment limitations, this is not possible on all sizes and permeabilities. Check with Magnetics for specific information and costs.

What about availability of parylene core coatings for toroids?

Parylene C® is a vacuum deposited coating providing good resistance to moisture and organic solvents. Electrical characteristics are superior to other coatings. Because this is an expensive coating, the size range is economically limited to an outside diameter of 14 mm or less.

What are soft magnetic cores?

Magnetic materials can be divided into two classifications: soft and hard (sometimes called permanent). Permanent magnets are considered "hard" magnetic materials because their magnetism is permanently retained, a result that has been achieved by their manufacturing process. Cores are considered "soft" magnetic materials because they are magnetically biased only when wound with current-carrying wire. Hard magnets are fixed at one point on the B-H (or hysteresis) curve. Soft magnetic materials can be cyclically driven along portions of their B-H curves, making them usable for transformers and inductors. Magnetics® manufactures soft magnetic cores which are used in a variety of electronic applications.

What are effective core parameters?

Magnetic cores, particularly ferrites, are made in a variety of geometries. In order to apply the many formulas that are used in calculations for designs, core physical parameters are calculated to minimize geometry effects. These parameters are the magnetic path length, effective area and effective volume.

How does Magnetics measure toroid coating insulation and make voltage breakdown guarantees?

Core finishes on toroids are measured for voltage breakdown by inserting the core between two weighted wire mesh pads. The force is adjusted to produce a uniform pressure of 10 psi, simulating winding pressure. The test is conducted using a 60 Hz r.m.s. or DC voltage. Consult the toroid product catalog for specific finishes and their guaranteed voltage breakdowns. Users should be careful to note that their actual windings, especially when heavy wire is used, can cause mechanical stresses that are not present in the standard breakdown test; excessive stresses here can result in a lower , than expected breakdown. On the other hand, magnet wire is insulated, unlike the wire mesh test pads.

How do I know which Magnetics soft magnetic core to use?

There is no universal answer to this question, as selection depends on the application and application frequency. Any material selected is subject to tradeoffs. For instance, some materials may keep heat rise to a minimum and are expensive, but if one is willing to put up with more heat, perhaps a larger component or less costly one will do the job. With Magnetics design tools, you can find the appropriate Magnetics core in a multitude of ways. If the design tools are not able to provide the assistance you need, the knowledgeable Application Engineering staff will be available to assist you.

How do you demagnetize a core?

Drive the core under 60 HZ conditions (saturating alternately in a positive and negative direction) then slowly reduce the drive level over several cycles until it is reduced to zero. This action will reduce the residual magnetization point to the origin.

What happens to a core if you go above the Curie temperature?

Curie temperature is the temperature at which a material loses all of its magnetic properties. Beyond the Curie temperature, the core loses all useful properties in a circuit. Many cores have an insulated coating which would be ruined long before the Curie temperature is reached. (Coating temperature restrictions can be found in Magnetics' Design Manuals.).

Strip wound cores can have their magnetic characteristics permanently altered during exposure to the Curie temperatures. Conventional strip wound cores and powder cores generally have such high Curie temperatures (>450°С) that the materials may be damaged due to oxidation well below the Curie temperature. Manganese-zinc ferrites, on the other hand, will not be affected, except for the insulated coating on them. This is due to the low Curie temperatures (120°С to 300°С) of ferrites. Exceeding these temperatures is generally not high enough to alter the ceramic material structure. In general, the core's magnetic properties will be restored when the temperature is reduced to below the Curie temperature, as long as the material has not been oxidized or held at high temperature for extended period of times.

What is the maximum frequency at which you can operate a magnetic material?

Primarily, this depends on the type of material. Strip wound cores generally will have a maximum usable frequency lower than ferrites, because the resistivity is lower, resulting in high eddy currents and higher core losses. The thinner the strip material, the higher the usable frequency. On the other hand, core losses depend on the operational flux density of the design; thus, by reducing the flux density, a higher operating frequency can be achieved. Often in power magnetics, it is not the saturation flux density (Bsat) of the material that limits the drive level, but rather the maximum tolerable losses at the specific operating frequency. Consult the Magnetics' Design Manuals to see the relationships among core losses, frequency, and flux densities.

What is the relative cost of different magnetic materials?

Much of the cost is related to the basic cost of raw materials. Magnetic materials containing high percentages of nickel or cobalt have a higher cost than those containing primarily iron. In between these two extremes are the variety of compositions that comprise the many types of materials and geometries. Material cost impacts large cores more significantly than small ones. Relative costs can be compared as follows:

In powder cores, if the price of iron powder ranges from x-3x:
Kool Mμ® — ranges from 4x-5x
XFlux — approx. 6x-8x
High Flux — approx. 10x
MPP — approx. 12x

Ferrite cost is often a function of geometry: Toroids = Least expensive • E Cores = Mid-level expense • Other Shapes = Most expensive

Why do you put an air gap into cores?

Introducing an air gap into a core, "tilts" or "shears" the B-H loop, making it possible to use the core at higher H levels. It is desirable, for many applications such as inductors, to delay this saturation. Air gaps have an added advantage in allowing for tighter control on inductance.

What is magnetostriction?

When a magnetic material is magnetized, a small change in dimension occurs. The relative change is in the order of several parts per million, and is called "magnetostriction". For applications like ultrasonic generators, the mechanical motion produced by magnetic excitation through magnetostriction is used to good advantage. In other applications, operating in the audible frequency range, an unwanted audible hum is observed. For this reason, low magnetostrictive materials such as Permalloy 80, Kool Mμ® and MPP powder cores may be used to limit or remove audible noise.

How do you determine proper core size?

Two elements are useful in determining core size: core window (winding) area and core cross­ sectional area. The product of these two elements (area product, or WaAC) relates to the power handling capability of a core. The larger the WaAC) the higher the power able to be handled. As operating frequency increases, the area product can be reduced, thus reducing the core size. Magnetics publishes the area products as a useful design tool. Consult the Magnetics Design Manuals to see the relationships among core losses, frequency, and flux densities.

What are the differences between using a distributed gap (powder core) versus a discrete gap (ferrite)?

A distributed gap material such as Kool Mμ® has each alloy grain insulated from the others. This allows for soft saturation over increasing current, giving inherent fault protection. Discrete gap cores hold high inductance out to a knee in the curve resulting in sharp saturation. Distributed gap cores hold better Bmax and DC bias at high temperatures. Discrete gap cores have fringing flux around the gap adding significantly to the losses.

Where can I find core standards?

The organization recognized for new and existing core standards is the International Electrotechnical Commission (IEC). Specifically the group TC-51 works with core specifications - www.iec.ch (www.iec.ch).

What conversions are commonly used in magnetics design?

Multiply By To Obtain
Oersteds
Oersteds
Oersteds
ampere-turns/inch
Gausses
2,0213
0,79577
79,577
1,2566
10-4
ampere-turns/inch
ampere-turns/sm
ampere-turns/m
Oersteds
teslas

Application

What types of cores are used for transformers? What type for inductors?

Desirable materials for transformer cores are those that have a high flux density and keep the temperature rise within desirable limits. High permeability materials are desirable to limit the exciting current (air gap minimized). For lower frequency applications (under 20kHz), strip materials have the highest flux density; for higher frequency applications (above 20kHz), ferrites are desirable because the materials are designed to have low core losses (lower heat rise) at these higher frequencies.

For inductors, cores that have discrete or distributed air gaps are desirable because they can maintain their constant permeability levels up to high DC or AC drive levels. Ferrites and strip wound cores can be gapped. Powder cores have a built-in distributed air gap.

See Magnetics Core Selection Guide for selection by application.

Why does one consider single layer windings on toroid cores?

Single layer windings are less costly to wind. The distributed capacitance is kept to a minimum. Temperature rise due to copper loss is minimized. For common mode chokes, symmetry between the opposing windings is much easier to maintain when only one layer is used.

What is a bifilar winding?

This refers to two wire strands, usually twisted among themselves. This double wire is wound on a core or on a coil to obtain two windings of equal length and parallel to each other, used instead of one core of large diameter.

Assembly

Why does the inductance decrease after winding and potting?

Ferrite materials are susceptible to mechanical stress, both from winding the core and from encapsulation. High permeability materials are particularly affected. Suggested remedies: (1) after winding, bake, and or temperature cycle, (2) thin out epoxy used for encapsulation or dope with an inert material such as sand or ground mica, (3) cushion with tape.

How do I know the ferrite hardware will fit on the core?

Cores are manufactured to standards that have been agreed to in the industry Tolerances have been assigned to the critical dimensions. Generally, hardware fit should not be a problem. When possible hardware and cores should be purchased from the same source.

Powder Cores

Can you press powder cores to different heights?

Many cores can be pressed to different heights. Dies are made so that the cavities can accommodate a range of heights. Height variation is relative to core size. One advantage this offers is the ability to produce alternate core sizes with out the expense of additional tooling. Consult our specialists for specific questions on the size of interest.

In powder cores, why is measured inductance different from calculated?

Magnetics measures Inductance in a Kelsall Permeameter Cup. Actual wound inductance outside a Kelsall Cup is greater than the value calculated due to leakage flux and flux developed in the winding. The difference depends on the core size, permeability, core finish thickness, wire size, and number of turns, in addition to the way windings are put on the core. The difference is negligible for 125μ and higher and turns greater than 500. The following table is a guide to the differences that one might experience:

Number of turns Actual L Number of turns Actual L
1000
500
300
0%
+0,5%
+1,0%
100
50
25
+3,0%
+5,0%
+8,5%

What is the main advantage of each distributed gap material?

Powdered Iron is the least expensive material, while MPP has the lowest losses and the best Q. High Flux has the highest DC bias. Kool Mμ® is a mix of the advantages of the previous three; lower losses than Iron Powder, near zero magnetostriction, and much lower cost than MPP. XFlux®can be a lower cost alternative to High Flux in situations where higher core losses are acceptable. New K Kool Mμ® MAX offers high DC bias and super low losses similar to MPP, which is the optimal solution for high efficiency, high power inductors.

What is the adhesive recommended for Powder Cores?

Resinlab EP950G is a one part epoxy adhesive that is recommended for use on powder core materials. This adhesive has good strength at room temperature and retains strength at high temperatures.

How are properties affected when cores are stacked?

Stacking cores will increase the cross section (Ae) by the multiple of the number of cores in the stack. The magnetic path length (le) will remain constant. The AL can be estimated by the same method as for single sets, where a leakage adjustment is estimated based on the ratio of window area (WA) to core area (Ae). Because that ratio decreases as cores are stacked, the AL of n stacked sets are slightly less than n times the L of a single set.

What is soft saturation?

Soft saturation is a distributed gap material advantage over a ferrite. The DC bias curve does not have the traditional saturation point that a ferrite core does, rather, as the drive level increases the permeability slowly rolls off in a predictable fashion.

Ferrites

How important is permeability in power materials?

Permeability is flux density, (B), divided by drive level, (H) Power materials are generally used for high frequency transformer applications. Hence, the important characteristics are high flux density and/or low core losses. Permeability is of lower importance because of its variability over an operating flux range.

What is disaccommodation?

Disaccommodation, occurring in ferrites, is the reduction of permeability with time after a core is demagnetized. This demagnetization can be caused by heating above the Curie point, by applying an alternating current of diminishing amplitude, or by mechanically shocking the core. In this phenomenon, the permeability increases towards its original value, then starts to decrease exponentially. If no extreme conditions are expected in the application, permeability changes will be small because most of the change has occurred during the first few months after manufacture of the core. High temperature accelerates the decrease in permeability. Disaccommodation is repeatable with each successive demagnetization; thus, it is not the same as aging.

Why are actual core losses larger than calculated?

When calculating the core losses, 1t is assumed that the structure is homogeneous. In reality, when core halves are mated, there is leakage flux (fringing flux) at the mating surfaces, and the gap losses contribute to the total losses. Gap losses are caused by flux concentration in the core and eddy currents generated in the windings. When a core is gapped, this gap loss can drastically increase overall losses. Additionally, because the cross-sectional area of many core geometries is not uniform, local "hot spots" can develop at points of minimum cross section. This creates localized areas of increased flux density, resulting in higher losses at those points.

What is the difference between nickel-zinc and manganese-zinc ferrites?

MnZn materials have a high permeability, while NiZn ferrites have a low permeability. Manganese-zinc ferrites are used in applications where the operating frequency is less than 5 MHz. Nickel-zinc ferrites have a higher resistivity and are used at frequencies from 2 MHz to several hundred megahertz. The exception is common mode inductors where the impedance of MnZn material makes it the best choice up to 70 MHz and NiZn is recommended from 70 MHz to several hundred GHz.

Why, in some cases, is only the minimum AL listed in the core datasheet?

Permeability (and AL) varies with drive level. For power applications, there is no need to place a limit on the maximum AL A minimum AL translates into maximum excitation current.

ЧWhat is the proper clamping pressure for ferrites?

Generally, a recommended figure is about 700 kg/м² (100 lbs/sq. in.) of mating surface. For specific recommended pressures tor RM, PO, EP, and pot cores, consult the MAGNETICS Ferrite Design Manual.

Why do you flat-grind ferrite cores?

Cores are flat-ground on the mating surface because of the surface produced during the firing process. It is important for cores to mate with a minimum air gap to keep the gap losses low and to achieve optimum inductance.

Why do cores get lapped? What is the surface finish?

Lapping is an additional production process used to improve the quality of the interface surface of the cores. Typically, this operation is performed for cores with material permeability of 5000 and greater in order to achieve the maximum AL value for a given material. A mirror-like finish is the result. he surface roughness with conventional flat polishing is 0.5 - 1.0 microns, and the surface for a lapped core is 0.1 - 0.2 microns.

Why is the ferrite gapped tolerance not always ±3%?

Due to limitations of the machine performing the gapping, as the gap dimension decreases it is increasingly difficult to hold tight tolerances. As AL increases, the gap gets smaller and the tolerances increase. As the gap gets smaller, the mechanical tolerance becomes proportionately larger, in addition the influence of variation in the material permeability becomes greater A gap specified by its AL value yields a tighter tolerance than a gap specified by its physical dimensions

How do you glue ferrite cores?

Gluing should be done with thermosetting epoxy resin adhesives. The available range is very large. Important factors in the choice are the required temperature and viscosity. The economic curing temperature must not be above the maximum temperature to which the assembly may be safely raised. High viscosity resin can be difficult to apply. Low viscosity resin may run out of a poorfitted joint or may be absorbed by the porous ferrite material. Follow the manufacturer's instructions for a particular resin. Take care not to thermalshock ferrites; raising or lowering the core temperature too rapidly is dangerous. Ferrites will crack if changes in temperature exceed 5-10°C/min. In addition, care must be taken to match the adhesives' coefficient of thermal expansion (CTE) to that of the ferrite material. Otherwise, the resin may expand or contract more quickly than the ferrite; the result can be cracks that will degrade core properties.

What is Magnetics' specification for out of roundness on a ferrite toroid?

Out of roundness is controlled by mandating that cores meet overall dimensional tolerances for OD and ID while keeping enough cross section to meet the specified AL. Refer to the MAGNETICS Ferrite Design Manual for toroid physical dimension tolerances.

What is the difference between nylon and epoxy coatings for ferrite toroids?

They are similar. Nylon is thicker, and can stand temperatures up to 155°C. Epoxy is rated at 200°C. Nylon finishes are generally applied to cores ranging in 0.D. (outside diameter) from 12.7 mm to 29 mm. Very large and very small сores are coated with a epoxy finish. The voltage breakdown guarantee of nylon and epoxy coating is 1000 volts wire to wire. Nylon cushions better and is more resistant to solvents. Both finishes are held to the same electrical specifications.

 
NORTH-WESTERN LABORATORY: NEWS
 
09.10 19 

LEPCOS invites you to attend the Stand C23 at ChipEXPO 2019 exhibition, which will be held from 16 to 18 October 2019 in Moscow in the Expocentre, in the pavilion "Forum".

chip_expo



26.06 19 
According to the results of 2018 Lepcos has received "best ferrites seller 2018" seal of excellence from TDK company.



18.04 19 
Dear colleagues! We would like to draw your attention to the fact that, since December 2018, the package content of electrolytic capacitors has been changed.



 
 


«North West Laboratory» © 1999—2020

Development & support — Marina Kutuzova